Caesium hydrogen sulfate or cesium hydrogen sulfate is the inorganic compound with formula CsHSO4. This colorless solid is the caesium salt of bisulfate. It is obtained by combining Cs2SO4 and H2SO4[1]

Properties

Above 141 °C, CsHSO4 is a superionic conductor.[1] The rapid ionic conductivity arise especially in the range of these temperatures due to the high activity of protons.[2]

Based on the results of X-ray crystallography, the structure consists of tetrahedral sulfate centers that bridge caesium ions. The proton is associated with the oxygen on sulfate.[3]

CsHSO4 goes through three crystalline phases that are referred to as phase III, II, and I.[4] CsHSO4 is initially existing in phase III at a room temperature of 21 °C. Phase III ranges from 21 °C to 90 °C with a transition temperature of 90 °C to 100 °C between phase III and phase II. Phase II ranges from 90 °C to 140 °C. At 140 °C, CsHSO4 undergoes a phase shift from phase II to phase I.[5]

Phase III (21 °C to 90 °C) and Phase II (90 °C to 140 °C) are referred to as the monoclinic phases, in which CsHSO4 exhibits its lowest proton conductivity. As the crystalline structure’s temperature is raised, it will show variations in the unit cell volume and the arrangement of its hydrogen bonds, which will alter the ability of a CsHSO4 crystalline structure to allow the displacement of protons.

At 141 °C, the CsHSO4 crystal structure experiences a structural change from monoclinic phase II to a tetragonal phase, becoming phase I. Phase I has more elevated crystal symmetry and widened lattice dimensions. Phase I is noted as the superprotonic phase (strong conducting phase), which triggers an extreme growth in proton conductivity by four orders of magnitude, reaching 10 mS/cm. This makes the conductivity of CsHSO4 ten-fold stronger than the conductivity of a sodium chloride aqueous solution. In the superprotonic phase, the movement of an SO4 tetrahedron generates a disruption of the hydrogen bond network, which accelerates proton transfer.[5] The tetragonal anions available in the structure are accountable for the arrangement of the hydrogen bonds with the moving protons.[6]

Potential applications

The maximum conductivity of pure CsHSO4 is 10 mS/cm, which is too low for practical applications. In composites with SiO2, TiO2, and Al2O3) , the proton conductivity below the phase transition temperature is enhanced by a few orders of magnitude.[7]

Unlike hydrated protonic conductors, the absence of water in CsHSO4 provides thermal and electrochemical stability. Electromotive force (EMF) measurements in a humidified oxygen concentration cell verified the high ionic nature of CsHSO4 in its superprotonic phase.[8] Based on heat rotation, the voltage stayed the same for over 85 hours during the measurement, particularly at the high temperature.[8] These results, demonstrate the thermal independence from humidity-type environments. Additionally, the crystal structure of CsHSO4 allows for quick transport of smaller charged ions, resulting in efficient energy transfer in electrochemical devices.

References

  1. 1.0 1.1 Haile, Sossina M.; Boysen, Dane A.; Chisholm, Calum R. I.; Merle,Ryan B. (2001). "Solid acids as fuel cell electrolytes". Nature 410 (6831): 910–913. doi:10.1038/35073536. PMID 11309611. Bibcode2001Natur.410..910H. https://authors.library.caltech.edu/14197/2/HAInature01supp.pdf. 
  2. Sinitsyn, V. V. (2010). "Pressure effect on phase transitions in MeHAO4 superprotonic conductors (A = S, Se and Me = NH4, Rb, Cs)". Journal of Materials Chemistry 20 (30): 6226–6234. doi:10.1039/c0jm00052c. 
  3. Balagurov, A.M.; Beskrovnyi, A.I.; Savenko, B.N.; Merinov, B.V.; Dlouha, M.; Vratislav, S.; Jirak (1987). "The room temperature structure of deuterated CsHSO4 and CsHSeO4". Physica Status Solidi A 100: 3–7. doi:10.1002/pssa.2211000146. 
  4. Maja Mroczkowska-Szerszeń, Maciej Siekierski, Rafał Letmanowski, Michał Piszcz, Renata Cicha-Szot, Lidia Dudek, Sławomir Falkowicz, Grażyna Żukowska, and Magda Dudek. "Spectroscopic Verification of Extended Temperature Stability of Superionic Phase Obtained in Mechanosyntehsis Process for CsHSO4/Phospho-silicate Glass Composite." Oil and Gas Institute, Ul. Lubicz 25a, 31-503 Cracow, Poland/Warsaw University of Technology Faculty of Chemistry, Inorganic Chemistry and Solid State Technology Division Ul.Noakowskiego 3, 00-640 Warsaw, Poland 3AGH – University of Science and Technology, Faculty of Fuels and Energy, Al. Mickiewicza 30, 30-059 Cracow, Poland, n.d. Web.
  5. 5.0 5.1 Otomo, Junichiro; Shigeoka, Hitoshi; Nagamoto, Hidetoshi; Takahashi, Hiroshi (2005). "Phase transition behavior and proton conduction mechanism in cesium hydrogen sulfate/silica composite". Journal of Physics and Chemistry of Solids 66 (1): 21–30. doi:10.1016/j.jpcs.2004.07.006. Bibcode2005JPCS...66...21O. 
  6. Chan, Wing Kee. Structure and dynamics of hydrogen in nanocomposite solid acids for fuel cell applications. TU Delft, Delft University of Technology, 2011.
  7. Hiroki Muroyama, Toshiaki Matsui, Ryuji Kikuchi, and Koichi Eguchi. "Composite Effect on the Structure and Proton Conductivity for CsHSO4 Electrolytes at Intermediate Temperatures." (n.d.): n. pag. Department of Energy and Hydrocarbon Chemistry, Graduate School of Engineering, Kyoto University, Nishikyo-ku, Kyoto 615-8510, Japan, 13 Apr. 2006. Web.
  8. 8.0 8.1 Uda, Tetsuya, Dane A. Boysen, and Sossina M. Haile. "Thermodynamic, thermomechanical, and electrochemical evaluation of CsHSO 4." Solid State Ionics 176.1 (2005): 127-133.